Water Based Dacromet Coating Paint JH-9380



JH-9380is made up of three packs: A,B and C;
Pack A: It is silver gray slurry that mainly chemically combined with super fine flake Zn, super fine flake Al and organic additive.
Pack B: It is water solution that mainly combined with corrosion protecion additive, particular regulator water solution etc.
Pack C: It is the tackifier of the coating which mainly made up of cellulose white or yellowish powder.


Performance characteristics:
The film is silver white, good surface finish, high corrosion resistance, good coating.


Coating Process
Coating Process:


1. Mix Ratio


Pack A:16.0 kg
Pack B:24.0 kg (the quantity can be increased appropriately if spray coating)
Pack C:0-50 g (according to different viscosity demand )


2. Before Mixture, Keep weighted A&B into the water bath at 25±2℃ , then stir A to make metal slurry disperse uniformly by frequency mixer ,after A is fully evenly dispersed, reduce the agitating speed to 60r/min, and add B.


3. Add B to the stirring A slowly. At the moment, the barrel temperature will go up,when it reaches 35℃, startup refrigerating device to keep the barrel temperature constant at 35℃.


4. Stir the mixture about 1~2 hours fast after B added, then add C. C should be powdered if lump exist.(The barrel temperature should not be lower than 30℃, otherwise C will not be dissolved sufficiently .)Then stir 12 hours continuously.


5. The coating should be filtrated by 100 mesh stainless steel screen before pouring into dip barrel.


6. Temperature control device should be equipped with dip barrel to keep the temperature of coating at 20±2℃.
(If temp. is too high, the paint is liable to deteriorate, and viscosity will be effected.) The coating should be stirred circularly to keep evenly dispersed.


7. Test Specific gravity, PH, Temperature, Viscosity of coating every 8 hours if operate continuously.


Water Based Dacromet Coating Paint JH-9380
Mix Diagram
Mix Diagram:


Water Based Dacromet Coating Paint JH-9380


Other chemicals such as any kinds of acid, alkali salt can not be mixed into coating, for these can activate Zn & Al plate to aging the coating.


Avoid irradiation of sunshine and ultraviolet ray for long time when operating, otherwise it will accelerate aging or polymerization of the coating .


It is very important to control the temperature of coating. If the temperature of coating changes when operating, it will effect the viscosity, then effec the coating quatity on workpiece. So the relations among temperature,viscosity and spinning process shoud be controlled well when coating.


The viscosity will be different if coating method is different. Choose low data if spray coating,and choose high data if dip spin coating.
Technical data
Technical data:


2Coating methodDip Spin & Spraying
5Specific gravity1.33±0.05( spraying)1.33±0.05(dip-spin coating)
6Viscosity20~60s(Spray Coating) 60~90S(Dip-Spin Coating)
7Operating temperature20±2℃
Minimum Order Quantity:100 Kilograms
Packaging Details: Pack A:16kg/ Metal Barrel
                               Pack B:24KG Plastic Barrel
                               Pack C:Based on the amount of B agent A

Delivery Time: Ten days after receipt of advance payment
Supply Ability: 2 Tons per Day
Cr6+: ≥25g/L
Color: Silver
PH: 3.8-5.2
Specific Gravity: 1.33±0.05( Spraying)1.33±0.05(dip-spin Coating)
Viscosity: 20~60s(Spray Coating) 60~90S(Dip-Spin Coating) Operating Temperature: 20±2℃