Chrome Free Water Based Zinc Flake Coating Salt Fog Time 480 Hours JH-9310

Description
Description:

 

JH-9310 is made up of three packs: A,B and C;
Pack A: It is silver gray slurry that mainly chemically combined with super fine flake Zn, super fine flake Al and organic additive.
Pack B: It is water solution that mainly combined with corrosion protecion additive, particular regulator water solution etc.
Pack C: It is the tackifier of the coating which mainly made up of cellulose white or yellowish powder.

 

Performance Charcteristic:

 

Chrome free, film is silver grey to silver white, better corrosion protection performance.
Coating Process
Coating Process:

 

1. Mix Ratio
Pack A: Pack B: Pack C=1:1: X(according to different viscosity demand )

 

2. Before Mixture, Keep weighted A&B into the water bath at 25±2℃ , then stir A to make metal slurry disperse uniformly by frequency mixer ,after A is fully evenly dispersed, reduce the agitating speed to 60r/min, and add B.

 

3. Add B to the stirring A slowly.

 

4. Stir the mixture about 1~2 hours after B added, then add C. C should be powdered if lump exist.(The barrel temperature should not be lower than 20℃, otherwise C will not be dissolved sufficiently .)Then stir 12 hours alowly and continuously.

 

5. The coating should be filtrated by 80-100 mesh stainless steel screen before pouring into dip barrel.

 

6. Temperature control device should be equipped with dip barrel to keep the temperature of coating at 22±2℃.
(If temp. is too high, the paint is liable to deteriorate, and viscosity will be effected.) The coating should be stirred circularly to keep evenly dispersed.

 

7. Test Specific gravity, PH, Temperature, Viscosity of coating every 8 hours if operate continuously.

 

Chrome Free Water Based Zinc Flake Coating Salt Fog Time 480 Hours JH-9310
Mix Diagram
Mix Diagram:

 

Chrome Free Water Based Zinc Flake Coating Salt Fog Time 480 Hours JH-9310
Attentions
Attentions:

 

1. Other chemicals such as any kinds of acid, alkali salt can not be mixed into coating, for these can activate Zn & Al plate to aging the coating.

 

2. Avoid irradiation of sunshine and ultraviolet ray for long time when operating, otherwise it will accelerate aging or polymerization of the coating .

 

3. It is very important to control the temperature of coating. If the temperature of coating changes when operating, it will effect the viscosity, then effec the coating quatity on workpiece. So the relations among temperature,viscosity and spinning process shoud be controlled well when coating.

 

4. The viscosity will be different if coating method is different. Choose low data if spray coating,and choose high data if dip spin coating.
Technical data
Technical data:

 

No.ItemData
1ColorSilver
2Coating methodDiping & Spraying
3PH(20℃)5.0-8.0
4Specific gravity(20℃)1.30-1.40 (spray coating)
5ViscosityAccording to operating demand.
6Operating temperature22±2℃
left
Minimum Order Quantity: 100 Kiloamperes
Packaging Details: Pack A:20kg/ Metal Barrel
                               Pack B:20KG Plastic Barrel
                               Pack C:Based on the amount of B agent A

Delivery Time: Ten days after receipt of advance payment
Payment Terms: L/C, T/T
Supply Ability: 2 Ton/Tons per Day
right
Color: Silver
Coating Method: Dip-spin & Spraying
PH(20℃): 5.0-8.0
Specific Gravity: 1.30-1.40 (spray Coating)
Viscosity: According To Operating Demand.
Operating Temperature: 22±2℃